202 cold rolled stainless steel coil (0.2mm-3mm)

Short Description:

Thickness: 0.2mm – 3.0mm

Width: 600mm – 1500mm, the narrowed products pls check in strip products

Max coil weight: 10MT

Coil ID: 508mm,610mm

Finish: 2B,2D


Product Detail

Product Tags

Huaxiao Capacity about 202 cold rolled stainless steel coil, 202 CRC

Thickness: 0.2mm – 3.0mm

Width: 600mm – 1500mm, the narrowed products pls check in strip products

Max coil weight: 10MT

Coil ID: 508mm,610mm

Finish: 2B,2D

202 cold rolled stainless steel coil Same grade from different mill standard

202 L4, 202 J4, 202 J3

202 Chemical component  LISCO – L4 :

C:≤0.15 ,Si :≤1.0  Mn:7.0-10.0 ,Cr:14~16.00 ,Ni:3.5~6.5, S :≤0.03 ,P :≤0.06 Cu: < 2.0 , N≤0.2

202 mechanical property  LISCO – L4:

Tensile strength :  > 515 Mpa

Yield Strength :  >205 Mpa

Elongation (%):  > 35%

Hardness: < HRB95

Description about 202 cold rolled stainless steel coil

The advantage price of 202 cold rolled stainless steel coil is better than 304 stainless steel, most of the 200 series stainless steels sold on the Chinese market have almost no control of sulfur and carbon content in accordance with national standards, and manganese (and nitrogen) has replaced some or all of nickel to produce lower nickel content austenitic stainless steels.

 The disadvantages of this series of materials are: less than 18% of the chromium content and the low nickel content do not balance the formation of ferrite, for which the chromium content in the 200 series stainless steel is reduced to 13.5% to 15%, some The situation dropped to 13% to 14%, and its corrosion resistance could not be compared with 304 and other similar steels. In addition, manganese, and in some cases copper, reduce the effect of repassivation under the acidic conditions common in the corrosion sites of the deposition zone and crevices. The destruction rate of 200 series steel under these conditions is approximately 10-100 times that of 304 stainless steel. The residual sulfur content and carbon content in these steels are often not controlled during production, and the material cannot be traced back to the source, even in material recycling. If Cr-Mn steels are not specified, they will become a dangerous scrap mixed raw material, leading to castings containing unexpectedly high levels of manganese.

202 cold rolled stainless steel coil-02 202 cold rolled stainless steel coil-01