China Supplier 309 Stainless Steel Sheet - 316L316 Cold Rolled Stainless Steel sheets(0.2mm-8mm) – Huaxiao

Sino Stainless Steel Capacity about 316L 316 cold rolled stainless steel sheets, 316 316L CRC

Thickness:  0.2mm – 8.0mm

Width:  300mm – 6000mm, the narrowed products pls check in strip products

Package weight:  1.0-3.0MT

Finish:  2B,2D

316 Same grade from different country standard

06Cr17Ni12Mo2 0Cr17Ni12Mo2 S31600 SUS316 1.4401

316 Chemical component  ASTM A240 :

C: ≤0.08, Si: ≤0.75 　Mn: ≤2.0, S: ≤0.03, P: ≤0.045, Cr: 16.0～18.0, Ni: 10.0～14.0，

Mo: 2.0-3.0, N≤0.1

316 mechanical property  ASTM A240 :

Tensile strength :  > 515 Mpa

Yield Strength :  >205 Mpa

Elongation (%):  > 40%

Hardness: < HRB95

316L Same grade from different country standard

1.4404 022Cr17Ni12Mo2 00Cr17Ni14Mo2 S31603 SUS316L

316L Chemical Component  ASTM A240 :

C: ≤0.03, Si: ≤0.75 　Mn: ≤2.0, S: ≤0.03, P: ≤0.045, Cr: 16.0～18.0, Ni: 10.0～14.0，

Mo: 2.0-3.0, N≤0.1

316L Mechanical Property  ASTM A240 :

Tensile strength :  > 485 Mpa

Yield Strength :  >170 Mpa

Elongation (%):  > 40%

Hardness: < HRB95

Corrosion resistance

Corrosion resistance is better than 304 stainless steel, with good corrosion resistance in the production process of pulp and paper. Moreover, 316L stainless steel is also resistant to erosion by marine and aggressive industrial atmospheres.

Heat resistance

316L stainless steel has good oxidation resistance in intermittent use below 1600 °C and continuous use below 700 °C. In the range of 800-1575 degrees, it is best not to continue to act. 316L stainless steel, but when 316L stainless steel is continuously used outside this temperature range, the stainless steel has good heat resistance. 316L stainless steel has better carbide precipitation resistance than 316 stainless steel and can be used in the above temperature range.

Heat treatment

The solution annealing is performed in a temperature range of 1010-1150 degrees, and then rapidly cooled. 316L stainless steel cannot be hardened by heat treatment.

Welding performance

316L stainless steel has good welding properties. All standard welding methods can be used for welding. When welding, 316Cb, 316L or 309Cb stainless steel filler rods or welding rods can be used for welding according to the application. For best corrosion resistance, the welded section of 316 stainless steel requires post-weld annealing. If 316L stainless steel is used, post-weld annealing is not required.